45钢汽车稳定杆断裂失效分析
Analysis on the Fracture Failure of 45 Steel Automobile Stabilizing Rod
Received:March 29, 2010  Revised:July 10, 2010
DOI:
中文关键词: 45钢  稳定杆  失效分析
英文关键词: 45 steel  stabilizing rod  failure analysis
基金项目:
Author NameAffiliation
WANG Hui No.59 Research Institute of Ordnance IndustryChongqing 400039China 
MEI Hua-sheng No.59 Research Institute of Ordnance IndustryChongqing 400039China 
Hits: 4116
Download times: 3034
中文摘要:
      采用断口分析、显微组织检验、低倍组织检验和化学成份分析等方法,对45钢汽车稳定杆进行了失效分析。断裂失效的主要原因是由于材料的成分偏析、热处理工艺不当和表面缺陷造成的。建议改进热处理工艺,保证组织的均匀性;选用成分均匀的钢材。
英文摘要:
      The failure analysis of the automobile stabilizing rod which is made of 45 steel was made through fracture microscopic analysis, microstructure test, macrostructure test and chemical compositions analysis. The main causes of the fracture failure were composition segregation, improper heat-treating process and surface defect. Improving the heat-treating process to ensure the uniformity of microstructure and selecting the steel with uniform ingredients were suggested.
View Full Text   View/Add Comment  Download reader
Close

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

You are the852402visitor    渝ICP备15012534号-4

>Copyright:Journal of Netshape Forming Engineering 2014 All Rights Reserved

>Postal Code: Phone:Fax: Email:

>    

渝公网安备 50010702501719号