文章摘要
王国峰,刘永康,陈玉清,等.电沉积Ni-Co纳米镀层热稳定性研究及低温扩散连接应用[J].精密成形工程,2022,14(4):115-121.
WANG Guo-feng,LIU Yong-kang,CHEN Yu-qing,et al.Investigation on Thermal Stability of Electrodeposited Ni-Co Nano-coating and Application in Low Temperature Diffusion Bonding[J].Journal of Netshape Forming Engineering,2022,14(4):115-121.
电沉积Ni-Co纳米镀层热稳定性研究及低温扩散连接应用
Investigation on Thermal Stability of Electrodeposited Ni-Co Nano-coating and Application in Low Temperature Diffusion Bonding
投稿时间:2021-12-11  
DOI:10.3969/j.issn.1674-6457.2022.04.014
中文关键词: 电沉积  Ni-Co纳米镀层  热稳定性  低温扩散连接
英文关键词: electro-deposition  Ni-Co nano-coating  thermal stability  low-temperature diffusion bonding
基金项目:国家科技重大专项(MJZ-2018-G-59)
作者单位
王国峰 哈尔滨工业大学材料科学与工程学院哈尔滨 150001
哈尔滨工业大学 金属精密热加工国防重点试验室哈尔滨 150001 
刘永康 哈尔滨工业大学材料科学与工程学院哈尔滨 150001
哈尔滨工业大学 金属精密热加工国防重点试验室哈尔滨 150001 
陈玉清 哈尔滨工业大学材料科学与工程学院哈尔滨 150001
哈尔滨工业大学 金属精密热加工国防重点试验室哈尔滨 150001 
张靖轩 哈尔滨工业大学材料科学与工程学院哈尔滨 150001
哈尔滨工业大学 金属精密热加工国防重点试验室哈尔滨 150001 
王月林 沈阳飞机工业集团有限公司沈阳 110013 
摘要点击次数: 2336
全文下载次数: 966
中文摘要:
      目的 研究不同Co含量电沉积Ni-Co纳米镀层的热稳定性能及其扩散连接应用效果。方法 在TC4钛合金表面电沉积Ni-Co镀层,改变镀液中Co含量(0、5、20 g/L),利用金相显微镜(OA)和透射电镜(TEM)观察分析镀层800 ℃热处理前后的微观组织。在真空扩散设备中进行TC4钛合金低温扩散连接(800 ℃、1 h),利用万能拉伸机检测扩散连接接头的剪切性能。结果 添加Co元素不仅能够减小镀层晶粒至19.2 nm,还能够提高其热稳定性能。纯镍镀层在800 ℃热处理5 h后晶粒长大至17.2 μm,而Ni-20 g/L Co镀层晶粒在相同条件下仅长大到10.5 μm且生长初期并未发现异常长大晶粒。以2.5 μm厚的Ni-Co镀层为中间层进行TC4钛合金低温扩散连接,接头剪切强度高达543.4 MPa。结论 Co元素的添加降低了晶界能量,提高了Ni-Co镀层的热稳定性能;作为TC4钛合金扩散连接的中间层,提高了原子的扩散系数,实现了TC4钛合金低温扩散连接,对工程应用具有重要意义。
英文摘要:
      The work aims to study the thermal stability and diffusion bonding effect of electrodeposited Ni-Co nano-coating with different Co contents. The Ni-Co nano-coating on the matrix of TC4 titanium alloy was electrodeposited by adjusting the content of the Co element (0, 5, 20 g/L) in the plating solution. The microstructure of Ni-Co nano-coating before and after heat treatment at 800 ℃ was observed through metallographic microscope (OM) and transmission electron microscope (TEM). The low-temperature diffusion bonding (800 ℃, 1 h) of TC4 alloy occurred in vacuum diffusion facilities and the shear property was tested with a universal testing machine. The addition of the Co element not only decreased the grain size of Ni-Co coating to 19.2 nm but also improved the thermal stability. The grain size of pure Ni coating treated at 800 ℃ for 5 h reached 17.2 μm. However, the grain size of Ni-Co coating with 20 g/L Co can only grow to 10.5 μm at the same conditions and there was no abnormal growing grain in the early growth stage. The shear strength of the joint can reach 543.4 MPa in the low-temperature diffusion bonding process of TC4 titanium alloy with 2.5 μm thick Ni-Co coating as interlayer. The Co element not only reduces the grain boundary energy of Ni-Co coating but also improves the thermal stability of Ni-Co coating. As an interlayer in the diffusion bonding process of TC4 titanium alloy, the Ni-Co coating improves the diffusing coefficient of the atom, realizes the low-temperature diffusion bonding of TC4 titanium alloy and is of great significance to engineering applications.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第14869331位访问者    渝ICP备15012534号-4

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

    

渝公网安备 50010702501719号