于浩,程兆虎,钱怡君.超声波导入时初始温度对铝-硅合金组织的影响[J].精密成形工程,2011,3(5):47-49.
YU Hao,CHENG Zhao-hu,QIAN Yi-jun.Influence of Starting Temperature of Ultrasonic Treatment on the Structure of Al-Si Alloy[J].Journal of Netshape Forming Engineering,2011,3(5):47-49. |
| 超声波导入时初始温度对铝-硅合金组织的影响 |
| Influence of Starting Temperature of Ultrasonic Treatment on the Structure of Al-Si Alloy |
| 投稿时间：2011-03-11 修订日期：2011-09-10 |
| DOI： |
| 中文关键词: 超声波处理 Al-20%Si合金 微观组织 |
| 英文关键词: ultrasonic treatment Al-20%Si alloy microstructure |
| 基金项目: |
|
| 摘要点击次数: 3766 |
| 全文下载次数: 3277 |
| 中文摘要: |
| 采用高能超声波对Al-20%Si合金进行处理，控制Al-20%Si合金熔体温度在620～680 ℃，研究合金组织随超声波导入时熔体初始温度的变化规律。实验表明，随着导入超声波时熔体温度的升高，初晶硅形貌由粗大的板片状逐渐变成细小的颗粒状，超声波处理熔体的温度控制在660 ℃左右时，初晶硅的组织细小、圆整度高、分布均匀。 |
| 英文摘要: |
| Influence rules of the microstructures of Al-20%Si alloy treated by high-intensity ultrasonic in the starting temperature ranges between 620 ℃ and 680 ℃ were studied. The mechanism of microstructural refinement for the ultrasonic treated alloy was also discussed. With the rise of starting temperature the morphology of primary crystal silicon changed by a thick sheet into small particles gradually. The results indicated that finer primary phase could be obtained when the starting temperature was at about 660 ℃. |
|