曹泽宇,闫洪.T6热处理对1.0%CNTs@TiO2/2024复合材料腐蚀性能研究[J].精密成形工程,2021,13(6):165-170.
CAO Ze-yu,YAN Hong.Corrosion Resistance Property of 1.0%CNTs@TiO2/2024 Composites by T6 Heat Treatment[J].Journal of Netshape Forming Engineering,2021,13(6):165-170. |
| T6热处理对1.0%CNTs@TiO2/2024复合材料腐蚀性能研究 |
| Corrosion Resistance Property of 1.0%CNTs@TiO2/2024 Composites by T6 Heat Treatment |
| 投稿时间：2021-05-27 |
| DOI：10.3969/j.issn.1674-6457.2021.06.023 |
| 中文关键词: CNTs@TiO2/2024复合材料 T6热处理 微观组织 腐蚀性能 |
| 英文关键词: CNTs@TiO2/2024 composites T6 heat treatment microstructure corrosion resistance |
| 基金项目:江西省研究生创新专项资金(YC2019-S056) |
|
| 摘要点击次数: 1309 |
| 全文下载次数: 483 |
| 中文摘要: |
| 目的 研究T6热处理对1.0%CNTs@TiO2/2024(CNTs质量分数为1.0%)微观组织和腐蚀性能的影响，以期提高2024复合材料的耐腐蚀性能。方法 通过熔铸法制备CNTs质量分数为1.0%的CNTs@TiO2/2024复合材料，并研究了T6热处理(495 ℃，2 h+180 ℃，4~16 h)对CNTs质量分数为1.0%的CNTs@TiO2/2024复合材料微观组织和腐蚀性能的影响。结果 经固溶处理(495 ℃，2 h)，S相(Al2CuMg)和θ相(Al2Cu)基本融入基体中;在时效处理(180 ℃，12 h)后，S相和θ相均匀析出。当加入CNTs质量分数为1.0%的CNTs后，与2024合金相比，复合材料的腐蚀电流密度大幅度增加了77.4%。与2024合金相比，T6态复合材料的腐蚀电位增加了4.4%，腐蚀电流密度下降了80.9%。结论 CNTs的加入会降低2024合金耐腐蚀性能，但是合适的T6处理工艺能够很好地提升其耐腐蚀性能，有效拓宽该系复合材料的应用领域。 |
| 英文摘要: |
| The work aims to investigate the effect of T6 heat treatment on microstructure and corrosion resistance of 1.0%CNTs@TiO2/2024 composites (mass fraction 1.0%) to improve the corrosion resistance of 2024 composites. 1.0%CNTs@TiO2/2024 composites were prepared by melt casting and then the effect of T6 treatment (495 ℃, 2 h+180 ℃, 4- 16 h) on the microstructure and corrosion resistance property of 1.0%CNTs@TiO2/2024 composites were studied. After solution treatment (495 ℃, 2 h), the S phase (Al2CuMg) and the θ phase (Al2Cu) were basically mixed into the matrix. After aging treatment (180 ℃, 12 h), both S phase and θ phase precipitated uniformly. When 1.0%CNTs was added, the corrosion current density of the composite increased by 77.4% compared with that of 2024 alloy. The corrosion potential of T6 composites increased by 4.4%, while the corrosion current density decreased by 80.9%, compared with 2024 alloy. The addition of CNTs will reduce the corrosion resistance of 2024 alloy, but the appropriate T6 treatment process can improve the corrosion resistance of 2024 alloy, and effectively broaden the application field of the composites. |
|