黑爱卿,邓全得,高斌,等.S-07钢在高压充气阀芯中的替代应用研究[J].精密成形工程,2020,12(3):172-177.
HEI Ai-qing,DENG Quan-de,GAO Bin,et al.The Application of S-07 Steel in High Pressure Gas-filled Valve Core[J].Journal of Netshape Forming Engineering,2020,12(3):172-177. |
| S-07钢在高压充气阀芯中的替代应用研究 |
| The Application of S-07 Steel in High Pressure Gas-filled Valve Core |
| 投稿时间：2019-12-04 修订日期：2020-05-10 |
| DOI：10.3969/j.issn.1674-6457.2020.03.022 |
| 中文关键词: 阀芯 S-03钢 渗氮 S-07钢 |
| 英文关键词: valve core S-03 steel nitriding S-07 steel |
| 基金项目: |
|
| 摘要点击次数: 2563 |
| 全文下载次数: 1579 |
| 中文摘要: |
| 目的 解决高压充气阀S-03钢渗氮阀芯生产过程中周期长、合格率低、渗氮层开裂和贮存过程中锈蚀及方向漏率超标等问题。方法 结合S-03钢渗氮阀芯工艺流程，分析其生产及贮存过程中存在的问题，并提出由S-07钢替代S-03钢渗氮工艺，从防锈、硬度和强度3个方面进行两种材料特性理论分析，同时进行耐蚀性试验、功能性试验、力学环境试验和寿命试验考核。结果 S-03钢渗氮阀芯经历湿热试验20 d后，出现轻微锈蚀，盐雾试验96 h后，锈蚀严重，而同条件下的S-07钢阀芯无锈蚀。S-07钢阀芯经过了功能性试验，x，y，z这3个方向的力学环境试验，动作200次的寿命考核试验后，动作灵活，功能测试合格。结论 充气阀阀芯完成了S-07钢替代工艺研究，成功解决了影响充气阀功能的阀芯锈蚀问题和渗氮层开裂问题，同时使生产效率提高了约70%，生产成本降低了约50%。 |
| 英文摘要: |
| The paper aims to solve the problems of long cycle, low qualification rate, cracking of nitriding layer, corrosion and reverse leakage rate in production of S-03 steel nitriding valve core of high pressure gas-filled valve. Combined with the technological process of S-03 steel nitriding valve, the problems existing in its production and storage process were analyzed. It was proposed to replace the nitriding process of S-03 steel with that of S-07 steel. The properties of two materials were theoretically analyzed from rust resistance, hardness and strength; at the same time, rust resistance test, functional test, mechanical environment test and life test were evaluated. After 20 days of damp-heat test, the S-03 steel nitriding valve core was slightly corroded; while after 96 h of salt spray test, the corrosion was severe; while the S-07 steel valve core was free from corrosion under the same condition. The S-07 steel valve core passed the functional test, the mechanical environment test in x, y and z directions, and the 200 times of life assessment test. The valve core was flexible and qualified in the functional test. The study on replacement technology of S-07 steel for the valve core is completed; the corrosion and nitrification layer cracking that affect the function of the valve is successfully solved; and the production efficiency is improved by about 70%, and the production cost is reduced by about 50%. |
|