秦鼎强,傅莉,倪昱,等.铝合金薄板高转速FSLW焊接界面形成及迁移行为[J].精密成形工程,2019,11(6):108-113.
QIN Ding-qiang,FU Li,NI Yu,et al.Formation and Migration Behaviour of Aluminium Alloy Thin Plate Welding Interface during High Rotational Speed FSLW[J].Journal of Netshape Forming Engineering,2019,11(6):108-113.
铝合金薄板高转速FSLW焊接界面形成及迁移行为
Formation and Migration Behaviour of Aluminium Alloy Thin Plate Welding Interface during High Rotational Speed FSLW
投稿时间:2019-08-29  修订日期:2019-11-10
DOI:10.3969/j.issn.1674-6457.2019.06.016
中文关键词: 2024铝合金薄板  高转速  搅拌摩擦搭接焊  焊接界面  迁移
英文关键词: 2024 aluminium alloy thin plate  high rotational speed  friction stir lap welding  welding interface  migration
基金项目:国家自然科学基金(51575450)
作者单位
秦鼎强 西北工业大学 材料学院 凝固技术国家重点实验室 陕西省摩擦焊接工程技术重点实验室西安 710072 
傅莉 西北工业大学 材料学院 凝固技术国家重点实验室 陕西省摩擦焊接工程技术重点实验室西安 710072 
倪昱 西北工业大学 材料学院 凝固技术国家重点实验室 陕西省摩擦焊接工程技术重点实验室西安 710072 
毛悦 西北工业大学 材料学院 凝固技术国家重点实验室 陕西省摩擦焊接工程技术重点实验室西安 710072 
肖旋 西北工业大学 材料学院 凝固技术国家重点实验室 陕西省摩擦焊接工程技术重点实验室西安 710072 
摘要点击次数: 2721
全文下载次数: 1911
中文摘要:
      目的 研究0.8 mm厚2024铝合金薄板在高转速搅拌摩擦搭接(FSLW)时对其焊接界面的影响规律。方法 通过采用铜粉作为标记材料,探究了高转速FSLW接头的微观组织、焊接界面形成及迁移的特征,揭示了高转速FSLW接头中转速对焊接界面迁移的影响规律。结果 焊接界面是由于原始界面上距焊缝中心线约轴肩半径距离的两侧金属因受到的热循环和机械力不足,难以形成原子间的结合,之后伴随塑性金属的流动,原始界面上距焊缝中心线约轴肩半径距离的两侧金属流向焊缝当中,进而形成未熔合界面。焊接界面的迁移是由于焊缝塑性金属发生了摩擦和挤压,进而引起了焊接界面的向上或向下迁移。结论 铝合金薄板高转速FSLW时,焊接界面在前进侧向上迁移,在后退侧向下迁移。随着转速增加,焊接界面迁移的垂直距离(沿板厚方向)逐渐减小。
英文摘要:
      The paper aims to study the effect law of 0.8 mm thick 2024 aluminium alloy sheet on the welding interface during high rotational speed FSLW. The microstructure, welding interface formation and migration characteristics of FSLW joints with high rotational speed were investigated with copper powder marker. The influence of the rotational speed on the welding interface migration in high rotational speed FSLW joints was revealed. The welding interface was the non-fusion interface formed by the metal on both sides of original interface from the weld centerline to about shoulder radius. Because of thermal cycling and insufficient mechanical force, the atomic bond was not formed but flowed with the flow of plastic metal into the weld. The migration of the welding interface was due to friction and extrusion of plastic metal, which caused upward or downward migration of the welding interface. The welding interface migrates upward at advancing side and migrates downward at retreating side. With the increase of rotational speed, the vertical distances (along the direction of the plate thickness) of the welding interface migration gradually decrease.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12072231位访问者    渝ICP备15012534号-6

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

>    

渝公网安备 50010702501719号