郎利辉,张闫飞,关世伟.基于单向拉伸的glare板力学性能测试[J].精密成形工程,2018,10(6):30-33.
LANG Li-hui,ZHANG Yan-fei,GUAN Shi-wei.Test on Mechanical Properties of Glare Plate Based on Uniaxial Tensile[J].Journal of Netshape Forming Engineering,2018,10(6):30-33.
基于单向拉伸的glare板力学性能测试
Test on Mechanical Properties of Glare Plate Based on Uniaxial Tensile
投稿时间:2017-10-16  修订日期:2018-11-10
DOI:10.3969/j.issn.1674-6457.2018.06.005
中文关键词: glare板  单向拉伸  成形性能  失效形式  断后伸长率
英文关键词: glare plate  uniaxial tensile  forming properties  failure form  elongation after fracture
基金项目:国家自然科学基金(51675029)
作者单位
郎利辉 北京航空航天大学 机械工程及自动化学院北京 100089 
张闫飞 北京航空航天大学 机械工程及自动化学院北京 100089 
关世伟 北京航空航天大学 机械工程及自动化学院北京 100089 
摘要点击次数: 3514
全文下载次数: 2582
中文摘要:
      目的 研究使用新方法制造小型大曲率glare板零件的可能性。方法 通过使用传统的模具来充液成形/普通拉深成形含有半固化玻璃纤维预浸料的glare板,成形后再进行固化。在室温下,使用单向拉伸方法分别对金属、含半固化玻璃纤维预浸料的glare板和固化之后的glare板进行力学性能测试。结果 含半固化玻璃纤维预浸料的glare板主要失效形式为金属板断裂,固化之后的glare板的主要失效形式为玻璃纤维断裂;含半固化玻璃纤维预浸料的glare板有着和金属相近的断后伸长率,具有较好的塑性,固化之后的glare板的断后伸长率远小于金属的断后伸长率,塑性极差。结论 通过使用传统的模具来充液成形/普通拉深成形含有半固化玻璃纤维预浸料的glare板,成形后再固化的方法来制造小型大曲率glare板零件是有可能的。
英文摘要:
      The paper aims to research the possibility of manufacturing small curvature glare plate parts with new method. Traditional molds are used for hydroforming/general drawing to form glare plates with semi-cured glass fiber prepreg to cure them after forming. Mechanical testings of glare plate with semi-cured glass fiber prepreg and glare plate were carried out at room temperature through uniaxial tension. Results show that glare plate containing semi-cured glass fiber prepreg mainly failed in fracture of metal plate. The main failure form of glare plate after curing was fracture of glass fiber; glare plate containing a semi-cured glass fiber prepreg had a similar elongation with metal, and had good plasticity. The elongation after fracture of glare plate after curing was far less than the elongation of metal. It is possible to have hydroforming/general drawing to form plate containing glare semi-cured glass fiber prepreg with traditional mold to manufacture small curvature glare plate parts after forming and curing.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12072988位访问者    渝ICP备15012534号-6

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

>    

渝公网安备 50010702501719号