单明东,夏益新,王娜,等.Al-Si镀层热成形零件表面颜色差异性研究[J].精密成形工程,2017,9(6):99-103.
SHAN Ming-dong,XIA Yi-xin,WANG Na,et al.Research on Surface Color Difference of Hot Stamping Part for Al-Si Coating[J].Journal of Netshape Forming Engineering,2017,9(6):99-103.
Al-Si镀层热成形零件表面颜色差异性研究
Research on Surface Color Difference of Hot Stamping Part for Al-Si Coating
投稿时间:2017-10-10  修订日期:2017-11-10
DOI:10.3969/j.issn.1674-6457.2017.06.019
中文关键词: Al-Si镀层  锌基镀层  热成形  表面颜色差异
英文关键词: Al-Si coating  Zn coating  hot stamping  surface color difference
基金项目:
作者单位
单明东 上海宝钢高新技术零部件有限公司上海 201908 
夏益新 上海宝钢高新技术零部件有限公司上海 201908 
王娜 上海宝钢高新技术零部件有限公司上海 201908 
刘海涛 上海宝钢高新技术零部件有限公司上海 201908 
曹奇 上海宝钢高新技术零部件有限公司上海 201908 
张丹荣 上海宝钢国际经济贸易有限公司上海 200122 
摘要点击次数: 3577
全文下载次数: 3694
中文摘要:
      目的 研究加热温度、加热时间等工艺参数对Al-Si镀层材料在热成形过程中存在的表面颜色差异、镀层厚度和扩散层厚度的影响规律,及影响零件表面颜色差异的主要原因。方法 在不同加热时间及加热温度条件下,对厚度为1.0 mm的新日铁Al-Si镀层材料进行热冲压试验,测量热成形零件的镀层厚度和扩散层厚度,并对典型不同颜色零件表面进行SEM及EDS分析研究。结果 Al-Si镀层热成形零件表面颜色与加热温度和加热时间存在较好的对应关系,同时镀层厚度及扩散层厚度随着加热时间的增加及加热温度的提高而增大,Al-Si镀层热成形零件表面的颜色与镀层中不同铁氧化物的混合比例存在较好的对应一致性。结论 Al-Si镀层热成形零件表面颜色的状态可以间接反应镀层厚度及扩散层厚度。
英文摘要:
      The paper aims to study influences of technological parameters such as heating temperature and heating time on surface color differences of Al-Si coating material, influencing law on thickness of coating and inter-diffusion layer in hot stamping, and reasons of color difference on the surface of parts. The hot stamping test was carried out with 1.0 mm thick Al - Si coating material from Nippon Steel at different heating time and heating temperatures; and then the coating thickness and the inter-diffusion layer thickness of hot forming parts were measured; and the typical different surface color parts were analyzed and researched by SEM and EDS. There was a good correspondence relationship between surface color of Al-Si coating hot stamping parts and heating temperature & heating time. At the same time, the thickness of the coating and the inter-diffusion layer increased with the increase of heating time and heating temperature; and there was a good correspondence relationship between the hot stamping parts surface color with Al-Si coating and the mix proportion of different iron oxides during coating. The surface color of the hot stamping parts with Al-Si coating can indirectly reflect thickness of the coating and the inter-diffusion layer.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12082318位访问者    渝ICP备15012534号-6

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

>    

渝公网安备 50010702501719号