菅宝柱,蒋清华,米丰亮,等.非调质钢曲轴感应淬火裂纹失效分析[J].精密成形工程,2016,8(4):78-82.
JIAN Bao-zhu,JIANG Qing-hua,MI Feng-liang,et al.Failure Analysis of Induction Hardening Crack for Non Quenched and Tempered Steel Crankshaft[J].Journal of Netshape Forming Engineering,2016,8(4):78-82.
非调质钢曲轴感应淬火裂纹失效分析
Failure Analysis of Induction Hardening Crack for Non Quenched and Tempered Steel Crankshaft
投稿时间:2016-05-18  修订日期:2016-07-10
DOI:10.3969/j.issn.1674-6457.2016.04.015
中文关键词: 非调质钢  感应淬火  裂纹分析
英文关键词: non quenched and tempered steel  induction hardening  analysis of crack
基金项目:
作者单位
菅宝柱 1. 山东大学 材料科学与工程学院济南 250061 2. 中国重汽集团济南铸锻中心济南 250116 
蒋清华 1. 山东大学 材料科学与工程学院济南 250061 2. 中国重汽集团济南铸锻中心济南 250116 
米丰亮 1. 山东大学 材料科学与工程学院济南 250061 2. 中国重汽集团济南铸锻中心济南 250116 
朱洪磊 1. 山东大学 材料科学与工程学院济南 250061 2. 中国重汽集团济南铸锻中心济南 250116 
王广春 山东大学 材料科学与工程学院济南 250061 
李建祖 中国重汽集团济南铸锻中心济南 250116 
摘要点击次数: 3577
全文下载次数: 3218
中文摘要:
      目的 分析非调质钢曲轴感应淬火时出现裂纹的原因。 方法 首先统计了裂纹的分布规律, 并确定了裂纹源位置,之后通过金相检验、低倍检验, 从锻打工艺、材料偏析等角度对裂纹进行了原因分析。 结果 产生在分模面位置的裂纹, 是因产品结构造成该区域材料在锻打过程中发生流速不均,当材料的框型偏析位置在锻造挤压下流动到此处时,偏析的材料产生了微细空洞,该微细空洞在后续感应淬火时成为裂纹源而引起开裂。 结论 该裂纹的产生与材料框型偏析有直接关系。 研究对控制非调质钢曲轴生产中的裂纹缺陷,提高曲轴生产质量, 具有重要应用价值。
英文摘要:
      To analyze the causes for induction hardening crack of non quenched and tempered steel crankshaft, this study firstly analyzed the crack distribution and determined the source of crack position, then analyzed the causes of cracks from the aspects of the forging process and material segregation through metallographic examination and acid corrosion test. According to the test results, crack in the position of parting surface was caused by the uneven regional material flow during forging process due to the structure of product. When the material of the box type segregation position under the forging extrusion flowed to here, micro holes were formed on the segregated materials. The micro holes became sources of crack in the subsequent induction quenching and consequently caused cracking. Therefore, the existence of cracks is directly related to the segregation of the material frame. Research on crack control of non quenched and tempered steel crankshaft production has important application value for improving the production quality of crankshaft.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12081566位访问者    渝ICP备15012534号-6

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

>    

渝公网安备 50010702501719号