郭斌,张李超.Cold Metal Transfer (CMT)与CMT Advanced的异同研究[J].精密成形工程,2016,8(2):50-54.
GUO Bin,ZHANG Li-chao.The Difference of CMT and CMT Advanced[J].Journal of Netshape Forming Engineering,2016,8(2):50-54.
Cold Metal Transfer (CMT)与CMT Advanced的异同研究
The Difference of CMT and CMT Advanced
投稿时间:2015-12-23  修订日期:2016-03-10
DOI:10.3969/j.issn.1674-6457.2016.02.011
中文关键词: CMT  CMT Advanced  薄板焊接  区别
英文关键词: CMT  CMT Advanced  sheet welding  difference
基金项目:
作者单位
郭斌 华中科技大学武汉 430074 
张李超 华中科技大学武汉 430074 
摘要点击次数: 3932
全文下载次数: 4167
中文摘要:
      目的 CMT及CMT Advanced是奥地利Fronius公司开发的2种新型焊接方法。通过实验结合理论分析, 研究这两种焊接方法的区别。方法 在相同的热输入量情况下, 分别采用CMT及CMT Advanced方法进行铝合金薄板对接实验, 通过使用热电偶采集焊接过程的冷却曲线, 游标卡尺测量焊后的变形量及X射线法检测沿焊缝方向的残余应力来对两者进行比较。结果 CMT焊后平均变形量为9.25 mm, 残余应力为(287.2±49) MPa, CMT Advanced焊后平均变形量为8.56 mm, 残余应力为(248.7±45) MPa。结论 与CMT相比, CMT Advanced具有更低的热输入量, 更高的熔敷效率、 间隙搭桥能力及焊接稳定性。
英文摘要:
      CMT and CMT Advanced are two new welding methods which developed by an Austrian company Fronius. This article describes the difference of these two welding methods through experimental and theoretical analysis. In order to compare these two welding methods, CMT and CMT Advanced are used for the experiments of aluminum alloy sheet docking in the context of same heat input, and using thermocouples to gather the cooling curve of welding process,using vernier caliper to measure the deformation after welding and using X-ray to detecte the residual stress along weld. The results showed that average deformation of CMT is 9.25 mm,residual stress of CMT is (287.2± 49) MPa,while average deformation of CMT Advanced is 8.56 mm, residual stress of CMT Advanced is(248.7±45) MPa. Compared with CMT, CMT Advanced has a lower heat input, higher deposition efficiency, gap bridging ability and welding stability.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12077514位访问者    渝ICP备15012534号-6

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

>    

渝公网安备 50010702501719号