郑林,车路长,张津,等.预拉伸厚铝板内 部残余应力 与晶粒取向均匀性的研究[J].精密成形工程,2014,6(5):50-58.
ZHENG Lin,CHE Lu-chang,ZHANG Jin,et al.Internal Residual Stress and Texture Homogenization in Pre-stretch Aluminum Alloy Plates[J].Journal of Netshape Forming Engineering,2014,6(5):50-58. |
| 预拉伸厚铝板内 部残余应力 与晶粒取向均匀性的研究 |
| Internal Residual Stress and Texture Homogenization in Pre-stretch Aluminum Alloy Plates |
| 投稿时间：2014-08-10 修订日期：2014-09-01 |
| DOI：10. 3969 /j. issn. 1674-6457. 2014. 05. 009 |
| 中文关键词: 预拉伸铝板 内 部残余应力 内 部织构均匀 性 短波长特征 X 射线 衍射 |
| 英文关键词: pre-stretch aluminum alloy plate internal residual stress internal texture homogenization short-wavelength characteristic X-ray diffraction |
| 基金项目:国 家高技术研究发展计划 (2009AA03Z539) ; 国 家重大科学仪器设备开发专项(2012YQ130234) |
| 作者 | 单位 | | 郑林 | 西南技术工程研究所, 重庆 400039 | | 车路长 | 西南技术工程研究所, 重庆 400039
国防科技工业精密塑性成形技术研究应用中心, 重庆 400039 | | 张津 | 北京科技大学 材料科学与工程学院, 北京 100083 | | 张鹏程 | 中国工程物理研究院 材料研究所, 绵阳 621700 | | 何长光 | 西南技术工程研究所, 重庆 400039 | | 彭正坤 | 西南技术工程研究所, 重庆 400039 | | 肖勇 | 西南技术工程研究所, 重庆 400039 | | 封先河 | 西南技术工程研究所, 重庆 400039 | | 朱蕾 | 西南技术工程研究所, 重庆 400039 |
|
| 摘要点击次数: 5114 |
| 全文下载次数: 3992 |
| 中文摘要: |
| 目 的 消减预拉伸铝板内 部残余应力。 方法 利 用 短波长 X 射线衍射仪( SWXRD) , 分别 对某公司 国 产 25 mm 厚 2024-T351 预拉伸铝板, 以 及美国 铝业公司 ( ALCOA) 20 mm 厚 7075 -T651预拉伸铝板的内 部残余应力、内 部织构及其沿板厚的分布, 进行了 无损测定。 结果 ALCOA 的 20mm 厚 7075 预拉伸铝板内 部残余应力小于 25 MPa, 其内 部晶 粒取向沿板厚均 匀 分布; 而某公司 原工艺生产的 25 mm 厚 2024 预拉伸铝板, 内 部残余应力高达 100 MPa 左右, 其内 部晶 粒取向沿板厚分布很不均匀 。 结论 源自 于轧制的内 部织构沿板厚分布的不均 匀 性, 使得以消 减残余应力 为 目的的预拉伸处理中的铝板塑性变形不均匀 , 导致某公司 国 产预拉伸铝板内 部残余应力 的 消 减效果差, 在其后续加工中容易产生加工变形超差的问 题, 需要抑制 强剪切织构的产生, 减小织构在整个板材厚度上的不均匀 分布程度。 |
| 英文摘要: |
| Objective To decrease the residual stress in pre-stretch plates. Methods The internal residual stress, internal texture and its distribution along the plate thickness were measured non-destructively for the domestic produced 2024 -T351 aluminum alloy pre-stretch plate with a thickness of 25 mm and the ALCOA 7075-T651 aluminum alloy pre-stretch plate with a thickness of 20 mm by means of the self- developed short- wavelength X - ray diffractometer ( SWXRD) . Results The results showed that the internal residual stress was less than 25 MPa and the internal texture was homogeneous along the plate thickness for the ALCOA 7075-T651 aluminum alloy plate, and the internal residual stress was much higher ( reaching about 100 MPa) and the internal texture was quite inhomogeneous along the plate thickness for the domestic 2024-T351 aluminum alloy plate. Conclusion The inhomogeneous distribution of the internal texture along the plate thickness led to the inhomogeneous plastic deformation of the aluminum plate in the pre-stretch treatment aimed to reduce the residue stress, and finally caused the poor reduction of internal residue stress by the domestic aluminum alloy pre-stretch plates. Therefore, suitable rolling process should be adopted to obtain homogeneous texture, and the strong shear texture should be restrained to increase the texture homogenization. |
|