文章摘要
马俊林,宋健,李萍.连接块温挤压模具强度校核及结构优化[J].精密成形工程,2014,6(3):36-40.
MA Jun-lin,SONG Jian,LI Ping.Strength Checking and Structure Optimization of Die for Connection Block of Warm Extrusion[J].Journal of Netshape Forming Engineering,2014,6(3):36-40.
连接块温挤压模具强度校核及结构优化
Strength Checking and Structure Optimization of Die for Connection Block of Warm Extrusion
投稿时间:2014-03-10  修订日期:2014-05-01
DOI:10.3969/j.issn.1674-6457.2014.03.008
中文关键词: 连接块  有限元模拟  温挤压成形  强度校核
英文关键词: connection block  FEM simulation  warm extrusion forming  strength checking
基金项目:
作者单位
马俊林 合肥工业大学 材料科学与工程学院, 合肥 230009 
宋健 合肥工业大学 材料科学与工程学院, 合肥 230009 
李萍 合肥工业大学 材料科学与工程学院, 合肥 230009 
摘要点击次数: 4562
全文下载次数: 3378
中文摘要:
      目的 解决铝合金连接块温挤压成形过程中出现的模芯开裂和上模载荷过大的问题。 方法 基于有限元软件 Deform-3 D 进行了三维有限元模拟,研究了连接块成形过程和模芯的受力状态。结果 结果表明,局部应力过大是导致模芯开裂的主要原??通过优化上模结构、增设溢流槽等措施以增大金属流动面积,可以显著降低模芯内腔局部应力和上模载荷。 结论 采用理论计算验证了 2 层组合凹模的安全性,有利于提高连接块的成形质量和凹模模芯的使用寿命。
英文摘要:
      Objective To solve the problem that core cracked and excessive load formed on the top die during the warm extrusion forming process of aluminum alloy connection block. Methods Simulation was conducted using Deform-3D, and the forming process and the state of the core were analyzed in the paper. Results The results showed that the main cause for cracks in the intra cavity of the core was the excessive local pressure. The load on the top die and the stress in the part where the cracks easily appeared were significantly reduced through improving the structure of top die, such as adding two spillway troughs. And it also increased the metal flow area. Conclusion The security of the two-layer assembled cavity die after optimization of the top die structure was confirmed using theory checking. As a result, the quality of connection block was improved and the life of the core was prolonged.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12072562位访问者    渝ICP备15012534号-6

>版权所有:《精密成形工程》编辑部 2014 All Rights Reserved

>邮编:400039 电话:023-68679125传真:02368792396 Email: jmcxgc@163.com

>    

渝公网安备 50010702501719号