姚春臣,佐齐生,易绯雄,等.2 A12 铝合金托盘开裂失效分析[J].精密成形工程,2013,5(4):57-59.
YAO Chun-chen,ZUO Qi-sheng,YI Fei-xiong,et al.Failure Analysis on Surface Cracks of 2 A12 Disks[J].Journal of Netshape Forming Engineering,2013,5(4):57-59. |
| 2 A12 铝合金托盘开裂失效分析 |
| Failure Analysis on Surface Cracks of 2 A12 Disks |
| 投稿时间：2013-05-23 修订日期：2013-06-01 |
| DOI：10.3969/j.issn.1674-6457.2013.04.015 |
| 中文关键词: 铝合金 托盘 冲压 热处理 失效分析 |
| 英文关键词: aluminum alloy disk stamping heat treatment failure analysis |
| 基金项目: |
|
| 摘要点击次数: 4114 |
| 全文下载次数: 3479 |
| 中文摘要: |
| 基于 2 A12 铝合金托盘表面处理后其底部加强筋上出现裂纹的情况,对其进行了理化分析、生产情况调查和验证试验后,认为其裂纹为托盘淬火后校形、压筋不及时,在材料有所硬化的情况下冲压而产生拉应力或导致冲压裂纹,表面处理使不太明显的裂纹变得明显。 托盘应在淬火后 1 . 5 h 内及时校形、压筋,防止材料时效硬化使冲压裂纹扩大。 |
| 英文摘要: |
| Some surface cracks on 2A12 disk ribs were found after surface treatment. Physical and chemical analysis and production investigation and verification were conducted, the results showed that the cracks were stamping cracks caused by sizing and pressing ribs after material hardening, and the surface treatment made it more serious. It was concluded that sizing and ribs pressing shoud be conducted after quenching in 1. 5 hours to prevent stamping cracks due to the material hardening. |
|