张志明,王长朋,庞丹,等.高强度钢热挤压模的失效分析[J].精密成形工程,2013,5(1):12-15.
ZHANG Zhi-ming,WANG Chang-peng,PANG Dan,et al.Failure Analysis of Hot Extrusion Mold for High-strength Steel[J].Journal of Netshape Forming Engineering,2013,5(1):12-15. |
| 高强度钢热挤压模的失效分析 |
| Failure Analysis of Hot Extrusion Mold for High-strength Steel |
| 投稿时间：2012-09-25 修订日期：2012-12-01 |
| DOI：10.3969/j.issn.1674-6457.2013.01.004 |
| 中文关键词: 热挤压工艺 模具 失效 断口 金相 热处理 |
| 英文关键词: hot extrusion mold failure fracture metallogaphy heat treatmen |
| 基金项目:国防基础科研重点项目( A1020110004) |
|
| 摘要点击次数: 4358 |
| 全文下载次数: 3559 |
| 中文摘要: |
| 通过扫描电镜、金相试验等方法,对高强度钢深孔热挤压模具冲头的失效进行了断口形貌及金相分析,判断出了模具失效的原因,并在模具材料的热处理工艺上提出了改进措施。 |
| 英文摘要: |
| Through the scanning electron microscope( SEM) , metallographic experiment, a fracture morphology analysis and metallography analysis on the failure of deep hole hot extrusion die for high strength steel are accomplished, the reason of mold failure is found, and the improvement measures to heat treatment process on the mold material is put forward. |
|